HDPE—High Density Polyethylene

specification:

Item

Test  condition

Test  method

Test  data

Unit 

Basic  

Properties

Melt  Floe  Rate

190° C/2.16kg

ASTM  D-1238

20

g/10min

Density

---

ASTM  D-792

0.954

g/cm3

Mechanical  

Properties

Hardness

---

ASTM  D-2240

57

Shore  D

2%Secant  flexural  modulus

---

ASTM  D-790  B

167, 000(1151)

psi(MPa)

Tensile  Strength  at  Break

---

ASTM  D-638

2000(14)

psi(MPa)

Tensile  strength  at  yield

---

ASTM  D-638

4100(28)

psi(MPa)

Elongation  at  break

---

ASTM  D-638

250

%

Yield  strain

---

ASTM  D-638

7

%

Tensile  Impact  Strength

---

ASTM  D-1822, Type  S

20(42)

ft? lb/in2(kJ/m2)

Resistance  to  environmental 

 stress  cracking  resistance

122? H(50° C), F50, 100%lgepal, hrs

ASTM  D-1693

3

---

Heat  

properties

Brittle  Temperature

---

ASTM  D-746

< -105(< -76)

? H(° C)

Heat  Deflection  Temperature

66psi(0.45MPa)

ASTM  D-648

163(73)

? H(° C)

Vicat  Softening  Point

---

ASTM  D-1525

261(127)

? H(° C)

DSC  melt  point

---

Dow  Method

266(130)

? H(° C)

DSC  Crystallization  point

---

Dow  Method

243(117)

? H(° C)

 

 

Grade: film grade,pipe grade,coating grade,bottle grade,fiber grade,etc

Tech grade: nature grade, recycle grade

Colour: nature transparent, white , black,etc ( or as client request)

Packing: 25kg/bag ( or as client request)

 

Use:

Virgin and Recycle Polyethylene Resin HDPE is widely used in the production of T-shirt bags, shopping bags, food bags, garbage bags, packaging bags, industrial lining and multilayer film, the resin can also be used in the production of anti-seepage film used in hydraulic engineering.